The heterogeneous integration of III–V devices with Si-CMOS on a common Si platform has shown great promise in the new generations of electrical and optical systems for novel applications, such as HEMT or LED with integrated control circuitry. For heterogeneous integration, direct wafer bonding (DWB) techniques can overcome the materials and thermal mismatch issues by directly bonding dissimilar materials systems and device structures together. In addition, DWB can perform at wafer-level, which eases the requirements for integration alignment and increases the scalability for volume production. In this paper, a brief review of the different bonding technologies is discussed. After that, three main DWB techniques of single-, double- and multi-bonding are presented with the demonstrations of various heterogeneous integration applications. Meanwhile, the integration challenges, such as micro-defects, surface roughness and bonding yield are discussed in detail.

High-performance GaInP/AlGaInP multi-quantum well light-emitting diodes (LEDs) grown on a low threading dislocation density (TDD) germanium-on-insulator (GOI) substrate have been demonstrated. The low TDD of the GOI substrate is realized through Ge epitaxial growth, wafer bonding, and layer transfer processes on 200 mm wafers. With O2 annealing, the TDD of the GOI substrate can be reduced to ～1.2×106 cm 2. LEDs fabricated on this GOI substrate exhibit record-high optical output power of 1.3 mW at a 670 nm peak wavelength under 280 mA current injection. This output power level is at least 2 times higher compared to other reports of similar devices on a silicon (Si) substrate without degrading the electrical performance. These results demonstrate great promise for the monolithic integration of visible-band optical sources with Si-based electronic circuitry and realization of high-density RGB (red, green, and blue) micro-LED arrays with control circuitry.

In this paper, normal incidence vertical p-i-n photodetectors on a germanium-on-insulator (GOI) platform were demonstrated. The vertical p-i-n structure was realized by ion-implanting boron and arsenic at the bottom and top of the Ge layer, respectively, during the GOI fabrication. Abrupt doping profiles were verified in the transferred high-quality Ge layer. The photodetectors exhibit a dark current density of ～47 mA/cm2 at ?1 V and an optical responsivity of 0.39 A/W at 1550 nm, which are improved compared with state-of-the-art demonstrated GOI photodetectors. An internal quantum efficiency of ～97% indicates excellent carrier collection efficiency of the device. The photodetectors with mesa diameter of 60 μm exhibit a 3 dB bandwidth of ～1 GHz, which agrees well with theoretical calculations. The bandwidth is expected to improve to ～32 GHz with mesa diameter of 10 μm. This work could be similarly extended to GOI platforms with other intermediate layers and potentially enrich the functional diversity of GOI for near-infrared sensing and communication integrated with Ge CMOS and mid-infrared photonics.